Abstract This study aimed to evaluate the effect of different loading conditions on the mechanical behavior and stress distribution of a leucite-reinforced glass-ceramic. Plate-shaped ceramic specimens were obtained from leucite-reinforced glass-ceramic (1.5 × 8.4 × 8.3 mm) and adhesively cemented to a dentin analog substrate. Monotonic and cyclic contact fatigue tests were performed to simulate sphere-to-flat contact, using a 6 mm diameter spherical piston; and flat-to-flat contact, using a 3 mm diameter flat piston. For the monotonic test (n=20), a gradual compressive load (0.5 mm/min) was applied to the specimen using a universal testing machine. Failure load data were analyzed with Weibull statistics. The cyclic contact fatigue test was performed using protocols (load and a number of cycles) defined by the boundary technique (n=30). Fatigue data were analyzed using an inverse power law relationship and Weibull-lifetime distribution. The stress distribution was investigated using Finite Element Analysis (FEA). The monotonic and the fatigue Weibull modulus were similar among the two contact conditions. In fatigue, the slow crack growth exponent was greater for sphere-to-flat contact, which indicates that the load level had a greater effect on the specimen’s probability of failure. In conclusion, FEA showed different stress distribution for the tested loading conditions. The stress distribution and probability of fatigue failure of specimens tested in sphere-to-flat contact showed greater dependency to load level.

Resumo O objetivo deste estudo é avaliar o efeito de diferentes condições de carregamento no comportamento mecânico e na distribuição de tensões de uma vitrocerâmica reforçada com leucita. Amostras cerâmicas em forma de lâminas foram obtidas a partir de vitrocerâmica reforçada com leucita (1,5 × 8,4 × 8,3 mm) e cimentadas adesivamente a um substrato análogo de dentina. Ensaios de carga de compressão monotônica e fadiga foram realizados para simular o contato esfera-plano, usando um pistão esférico de 6 mm de diâmetro; e contato plano com plano, usando um pistão plano de 3 mm de diâmetro. Para o ensaio de carga de compressão monotônica (n=20), foi aplicada uma carga compressiva gradual (0,5 mm/min) ao corpo-de-prova usando uma máquina de ensaio universal. Os dados de carga de fratura foram analisados de acordo com a distribuição de Weibull. O teste de fadiga foi realizado com os protocolos (carga e número de ciclos) definidos pela técnica de boundary (n=30). Os dados de fadiga foram analisados usando uma relação de tempo de vida - tensão de lei da potência inversa (IPL- inverse power law). A distribuição de tensões foi investigada usando análise de elementos finitos (AEF). O módulo de Weibull para teste de compressão monotônico e de fadiga foram semelhantes entre as duas condições de contato. Em fadiga, o expoente de crescimento sub-crítico da trinca foi maior para o contato esfera-plano, o que indica que o nível de carga teve um efeito maior na probabilidade de falha do corpo-de-prova. Em conclusão, AEF apresentou distribuição de tensões diferente para as condições de carregamento testadas. A distribuição de tensões e a probabilidade de falha em fadiga dos corpos-de-prova testados utilizando o contato esfera-plano apresentaram maior dependência do nível de carga.

O ameloblastoma é um tumor odontogênico benigno, porém agressivo, de origem epitelial, constituindo cerca de 1-3% de todos os tumores e cistos da mandíbula. Apresenta crescimento lento e persistente, localizado na maior parte dos casos na área de ramo de mandíbula e ocasionalmente associado com terceiros molares inclusos. As lesões são caracterizadas por uma infiltração agressiva para o tecido adjacente e as células tumorais restantes podem levar a morbidades múltiplas de recorrência. Dessa forma, pode ocorrer uma elevada taxa de recorrência local se não for adequadamente removido. Este artigo relata um caso de ameloblastoma multicístico previamente tratado com terapia conservadora que resultou no insucesso do tratamento e recidiva da lesão após oito anos. O exame clínico demonstrou extensa reabsorção óssea na região de hemimandíbula direita. Foi realizada biópsia incisional e exame histopatológico para confirmação diagnóstica. O tratamento proposto foi a ressecção total em bloco envolvendo além de hemimandíbula direita, a região de elementos dentários 31 e 32 com margem de segurança de dois centímetros. O protocolo radical cirúrgico com boa margem de segurança deve ser a opção para prevenir a recidiva destes tumores agressivos.

Ameloblastoma is an aggressive, benign odontogenic tumor of epithelial origin. Approximately 1-3% of all tumors and cysts of the maxillary bones are ameloblastomas. They grow at a slow but persistent rate and are mainly located in the ramus of the mandible. They are occasionally associated with the presence of an impacted third molar. Ameloblastomas are characterized by aggressive infiltration of the surrounding tissue. There may be a high local recurrence rate when the tumor is not properly removed, due to remaining tumor cells. This article reports a case of a multicystic ameloblastoma that had been previously treated with conservative therapy which failed and resulted in recurrence eight years later. Clinical examination showed extensive bone resorption in the right hemi-mandible region. Incisional biopsy and histopathological examination was carried out to confirm the diagnosis. The proposed treatment was total en bloc resection involving the right hemi-mandible, and the region of central and lateral left incisors with a two-centimeter safety margin. Radical surgical protocol with wide margin of safety must be adopted in order to prevent the recurrence of these aggressive tumors.

O objetivo deste estudo foi avaliar, in vitro, a liberação de flúor (F), ao longo do tempo, de três sistemas adesivos: Clearfil Protect Bond (CPB-Kuraray), FL Bond II (FLB-Shofu), Adper Single Bond 2 (SB2-3M ESPE) (controle negativo). Os sistemas adesivos CPB e FLB contêm flúor em sua composição e liberam F por diferentes mecanismos. A hipótese testada foi a de que o mecanismo de liberação de F influencia a quantidade de F liberado em água. Foram confeccionados espécimes em forma de discos (5 mm × 3 mm) utilizando uma matriz de plástico (Demetron Research Corp). Foram produzidas 3 amostras para cada um dos materiais, para cada período de avaliação (n=3) (1, 7, 14, 21 e 28 dias). Subsequentemente, as amostras foram armazenadas em 10 mL de água destilada a 37 °C até o momento das leituras que foram feitas usando uma membrana líquida para eletrodo seletivo de íons F (Orion 710). Foram realizadas quatro leituras no primeiro dia; após foi feita uma leitura/dia. Os resultados foram analisados estatisticamente por ANOVA e teste de Tukey (α=0,05). O sistema adesivo CPB liberou a maior quantidade de flúor em todos os períodos avaliados, com o maior valor em 6 H (0,183 ppm), então ela diminuiu gradualmente até o sétimo dia, quando aumentou significativamente até o dia 21. Na maioria das análises realizadas, FLB mostrou valores de liberação de flúor semelhantes aos de SB2. Portanto, o mecanismo de liberação de flúor influenciou a quantidade de fluoreto de liberado em água, confirmando a hipótese do estudo.

The objective of this study was to evaluate in vitro the time-dependent fluoride (F) release from three adhesive systems: Clearfil Protect Bond (CPB - Kuraray), FL Bond II (FLB- Shofu) and Adper Single Bond 2 (SB2 - 3M ESPE) (negative control). CPB and FLB are fluoride containing adhesives that use different F releasing mechanisms. The tested hypothesis was that the F releasing mechanism influences the amount of released F in water. Disc-shaped specimens (5 mm × 3 mm) were fabricated using a plastic matrix (Demetron Research Corp). Three specimens were produced for each material and each period of evaluation (1, 7, 14, 21 and 28 days) (n=3). Subsequently, the specimens were stored in 10 mL distilled water at 37° C until the analyses were done using a liquid membrane for selective F ion electrode (Orion 710). Four readings were performed on the first day and the remaining evaluation times had one reading/day. Results were statistically analyzed by two-way ANOVA and Tukey's test (α=0.05). CPB released the greatest amount of fluoride in all evaluated periods with the greatest value at 6th h (0.183 ppm) thereafter decreasing gradually up to the 7th day when it significantly increased again until the 21st day. In most measurements, FLB showed similar mean fluoride release values as SB2. Therefore, the fluoride release mechanism influenced the amount of fluoride released in water, confirming the study hypothesis.

The objective of this study was to evaluate the flexural strength (σf) and hardness (H) of direct and indirect composites, testing the hypotheses that direct resin composites produce higher σf and H values than indirect composites and that these properties are positively related. Ten bar-shaped specimens (25 mm x 2 mm x 2 mm) were fabricated for each direct [D250 - Filtek Z250 (3M-Espe) and D350 - Filtek Z350 (3M-Espe)] and indirect [ISin - Sinfony (3M-Espe) and IVM - VitaVM LC (Vita Zahnfabrik)] materials, according to the manufacturer's instructions and ISO4049 specifications. The σf was tested in three-point bending using a universal testing machine (EMIC DL 2000) at a crosshead speed of 0.5 mm/min (ISO4049). Knoop hardness (H) was measured on the specimens' fragments resultant from the σf test and calculated as H = 14.2P/l², where P is the applied load (0.1 kg; dwell time = 15 s) and l is the longest diagonal of the diamond shaped indent (ASTM E384). The data were statistically analyzed using Anova and Tukey tests (α = 0.05). The mean σf and standard deviation values (MPa) and statistical grouping were: D250 - 135.4 ± 17.6a; D350 - 123.7 ± 11.1b; ISin - 98.4 ± 6.4c; IVM - 73.1 ± 4.9d. The mean H and standard deviation values (kg/mm²) and statistical grouping were: D250 - 98.12 ± 1.8a; D350 - 86.5 ± 1.9b; ISin - 28.3 ± 0.9c; IVM - 30.8 ± 1.0c. The direct composite systems examined produce higher mean σf and H values than the indirect composites, and the mean values of these properties were positively correlated (r = 0.91), confirming the study hypotheses.

This study evaluated the flexural strength (sf) and the diametral tensile strength (st) of light-cured composite resins, testing the hypothesis that there is a positive relation between these properties. Twenty specimens were fabricated for each material (Filtek Z250- 3M-Espe; AM- Amelogen, Ultradent; VE- Vit-l-escence, Ultradent; EX- Esthet-X, Dentsply/Caulk), following ISO 4049 and ANSI/ADA 27 specifications and the manufacturers’ instructions. For the st test, cylindrical shaped (4 mm x 6 mm) specimens (n = 10) were placed with their long axes perpendicular to the applied compressive load at a crosshead speed of 1.0 mm/min. The sf was measured using the 3-point bending test, in which bar shaped specimens (n = 10) were tested at a crosshead speed of 0.5 mm/min. Both tests were performed in a universal testing machine (EMIC 2000) recording the fracture load (N). Strength values (MPa) were calculated and statistically analyzed by ANOVA and Tukey (a = 0.05). The mean and standard deviation values (MPa) were Z250-45.06 ± 5.7; AM-35.61 ± 5.4; VE-34.45 ± 7.8; and EX-42.87 ± 6.6 for st; and Z250-126.52 ± 3.3; AM-87.75 ± 3.8; VE-104.66 ± 4.4; and EX-119.48 ± 2.1 for sf. EX and Z250 showed higher st and sf values than the other materials evaluated (p < 0.05), which followed a decreasing trend of mean values. The results confirmed the study hypothesis, showing a positive relation between the material properties examined.

O objetivo deste estudo foi avaliar a resistência adesiva à tração (sigmat) e ao cisalhamento (sigmas) de uma cerâmica à base de alumina infiltrada por vidro e reforçada com zircônia (IZ- Vita In-Ceram Zircônia) à resina composta, testando a hipótese de que o sistema de silicatização (SC- Cojet, 3M-ESPE) produz valores maiores de resistência adesiva do que demais tratamentos de superfície utilizados. Sessenta corpos-de-prova (cp) em forma de disco da IZ foram fabricados e testados de acordo com as instruções dos fabricantes e as normas ISO6872 e ISO11405. Após polimento até 1 µm, os cp foram divididos em 3 grupos (n = 20) de acordo com o tratamento de superfície aplicado: HF - ácido hidrofluorídrico a 9,5% (Ultradent) por 1 min; SB - jateamento com óxido de alumínio 25 µm por 10 s; SC - silicatização por 10 s. Silano (3M-Espe), adesivo (Single Bond, 3M-Espe) e um cilindro resinoso (Z100, 3M-Espe) foram aplicados na área de adesão (3,5 mm de diâmetro) e fotoativados. Dez cp por grupo (n = 10) foram testados para sigmat e os outros 10 cp para sigmas em uma máquina de ensaios universal (EMIC DL 2000) com velocidade de 1 mm/min. Os resultados foram analisados estatisticamente por ANOVA e Tukey (alfa = 0,05). Os valores médios e desvio padrão (MPa) para sigmat foram: HF - 3,5 ± 1,0a; SB - 7,6 ± 1,2b; SC - 10,4 ± 1,8c. Para sigmas, os resultados foram: HF - 10,4 ± 3,1A; SB - 13,9 ± 3,1B; SC - 21,6 ± 1,7C (p < 0,05). Os grupos mostraram o mesmo ranqueamento estatístico de valores em ambos os testes. A IZ tratada com SC demonstrou aumento significativo na média de resistência adesiva em ambos os testes, confirmando a hipótese inicial.

The objective of this study was to evaluate the tensile (sigmat) and shear bond strength (sigmas) of a glass-infiltrated alumina-based zirconia-reinforced ceramic (IZ - Vita In-Ceram Zirconia) to a composite resin, testing the hypothesis that silica coating (SC - Cojet, 3M-Espe) produces higher bond strength values than other ceramic surface treatments. Specimens were fabricated and tested according to the manufacturers' instructions, and to ISO6872 and ISO11405 specifications. Sixty IZ disk specimens were polished through 1 µm and divided into 3 groups (n = 20) according to the following surface treatments: HF - 9.5% hydrofluoric acid (Ultradent) for 1 min; SB - sandblasting with 25-µm aluminum oxide particles for 10 s; SC - silica coating for 10 s. Silane (3M-Espe), adhesive (Single Bond, 3M-Espe) and a composite resin cylinder (Z100, 3M-Espe) were applied and polymerized to the treated bonding area (3.5 mm in diameter). Ten specimens from each group (n = 10) were tested for sigmat and ten specimens were tested for sigmas, using a universal testing machine (EMIC DL 2000) at a crosshead speed of 1 mm/min. The data were statistically analyzed by ANOVA and Tukey tests (alpha = 0.05). The mean and standard deviation values (MPa) and statistical groupings for sigmat were: HF - 3.5 ± 1.0a; SB - 7.6 ± 1.2b; and SC - 10.4 ± 1.8c. For sigmas, the values were: HF - 10.4 ± 3.1A; SB - 13.9 ± 3.1B; and SC - 21.6 ± 1.7C (p < 0.05). The groups presented the same statistical ranking of mean values for both test methods. The SC-treated IZ ceramic presented a significant increase in mean bond strength values for both test methods, confirming the study hypothesis.